Vic Duffhues (JoVic Pottery, Ladysmith BC) has added a few more spray guns to his collection, making the options for creating greater depth and color on his final work much more fun, and definitely more interesting.
Each application is allowed to dry carefully before another application takes place, but in this particular approach, with less glaze being applied in the way it is sprayed, the waiting time is not extreme as it is with multiple dipped applications.
He’s clearly enjoying the work with this series of teapots and vases on the previously bisqued ware.
It will be fun to see the final results and I’ll be sure to post more pictures.
The making of quality stoneware pottery, whether functional or decorative, is far from a rapid process. Aside from clay preparation, pots made require careful drying before they can even be put through their first bisque fire. But just the making is a time consuming thing, especially for large vases that are thrown in two stages.
Getting the neck onto the base requires careful joining; after all, if the pot is not put together correctly, the neck would come free of the vase. Careful smoothing and finishing is needed.
Then there’s a process that allows us to get some color onto the pieces before a first firing–of course not until the pieces are bone dry. We often spray the work with engobes, or brush on slip.
Once the pottery is again bone dry, we’re able to place the work into the kiln for a first firing. We bring them up slowly and cool slowly as well to avoid any potential cracking or warping through this cycle.
The cooled pots then need waxing before we can glaze. If we didn’t wax the bottoms the pottery would end up stuck to the kiln shelves.
Once the waxing is finished, we can get on with the work of glazing. This is frequently a slow process because we tend to use multiple glazes and each coat must be completely dry before we add a next layer. Bisqued pottery is still somewhat porous, and the water base of the glazes is absorbed into the work, requiring careful and total drying between each step.
Some of our pottery is actually put through a few low temperature firings. This ensures that the first layers of glaze are fired on, allowing us to handle the pottery without smudging or accidentally removing some of the glazes. Though the glazes in this case have not reached a mature melt, they are stable enough to handle.
Fired on glazes really help with some of our more complicated glaze applications. Crawl glazes, for instance, cannot be applied to glazes unless they have already been fired on at a lower temperature. By their very nature, as reticulating glazes, they would pull up any immature glazes they were placed on and instead of an attractive crawl, exposing lovely sub-surface colors or glazes, they’d end up exposing some terrible peeling effect that exposed clay.
Each kiln load has us looking forward to seeing whether what we envision at the start of making our work actually lives up to our hopes.
With the glazes applied, the final drying begins.
Once we’re sure the pots are dry, we can carefully load the kiln. Great care must be taken with vertical vases that have crawl glazes applied near the base.
A slight bump and the glaze will fall off the pot, potentially leaving bare spots where they might not be desired, and also fusing to expensive kiln shelves or other kiln furniture.
Some of the final results pleased Jo Duffhues immensely–not so Vic. He’ll likely take the vases he’s not thrilled with and apply additional glazes for yet another re-fire.
I have to remind him that some of our customers love the pieces that he is not excited about at all. The trouble is that when we work we have an idea of the outcome we’re seeking, and if things don’t turn out that way, we tend to think it’s a failure. It’s very hard to get past that kind of negative response. But since I love these pieces, I think they’re a great success.
Yes, these are the vases that Vic is seen making in the images above. Now it’s just a question of who wins the argument–will they be fired once again?